Influence of cementite coarsening on the corrosion resistance of high strength low alloy steel - npj Materials Degradation
Rating:
0.0
Views:
55
Likes:
1
Library:
1
The impact of heat treatment on the initiation and progression of localized corrosion in E690 steel in a simulated marine environment was investigated systematically. The primary cause of localized corrosion was the presence of inclusions, which led to the dissolution of the distorted matrix surrounding them. In the initial stages of corrosion, localized corrosion resulting from inclusions was the predominant form.